2026-05-11T11:43:54Zhttps://riubu.ubu.es/oai/request

oai:riubu.ubu.es:10259/75022023-03-08T01:05:27Zcom_10259_4201com_10259_5086com_10259_2604col_10259_4505

Efecto del postprocesado mediante HIP a 850ºC / 200 MPa en el comportamiento a fatiga de la aleación Ti-6AI-4V fabricada mediante SLM Alegre Calderón, Jesús Manuel García, Ricardo Díaz Portugal, Andrés Cuesta Segura, Isidoro Iván Ti-6AI-4V Hot isostatic pressing Selective Laser Melting Fatigue bahaviour Microstructura Resistencia de materiales Ingeniería civil Strength of materials Civil engineering Comunicación presentada en: 5th Iberian Conference on Structural Integrity que corresponde con el 38 Congreso del Grupo Español de Fractura GEF2022 celebrado en Coimbra, Portugal del 30 de marzo al 1 de abril de 2022 Hot Isostatic Pressing (HIP) es una técnica de postprocesado termomecánico ampliamente utilizada en piezas fabricadas mediante Selective Laser Melting (SLM) para densificar el material y reducir los defectos internos intrínsecos que se originan durante la fabricación, como porosidad o la falta de fusión, los cuales tienen un gran impacto en la resistencia a fatiga del material. En este trabajo se presenta el efecto de un ciclo HIP, realizado a una presión de 200 MPa y una temperatura de 850ºC durante 2 horas, sobre el comportamiento a fatiga de una aleación Ti-6Al-4V fabricada por SLM. Se ha efectuado un análisis defectológico y microestructural de las diferentes situaciones analizadas (SLM as-built, SLM+HIP, material de referencia) con el objetivo de estudiar la relación de los defectos y la microestructura con la vida en fatiga. Los resultados muestran que el presente proceso de HIP permite una muy buena densificación del material, y permite obtener una microestructura con mínimos efectos de engrosamiento de la fase α, lo cual se traduce en unas buenas propiedades de fatiga comparables a las del material de referencia. Hot Isostatic Pressing (HIP) is a thermo-mechanical post-processing technique widely used to reduce the internal defects characteristic of additive manufacturing techniques (lack-of-fusion or entrapped-gas-pores), which have a great impact on the fatigue properties of the material. In this work, the effect of a HIP-cycle at a pressure of 200 MPa and a temperature of 850ºC for 2 hours, on the fatigue behaviour of a Ti-6Al-4V alloy manufactured by SLM is presented. Microstructural and fractographic analysis for the different conditions (SLM as-built, SLM+HIP, reference material) have been carried out in order to study the effect of defects and microstructure features on the fatigue life. The results indicate that the present HIP process allows a very good densification of the material and exhibiting a microstructure with minimal alpha-phase coarsening effects, obtaining good fatigue properties comparable to the reference material ones. Los autores desean agradecer la financiación recibida a través del proyecto de la JCyL referencia BU-002-P20, cofinanciada con fondos FEDER. 2023-03-07T12:24:43Z 2023-03-07T12:24:43Z 2022-06 info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion 2792-4246 http://hdl.handle.net/10259/7502 spa Revista española de mecánica de la fractura. 2022, V. 4, p. 171-176 https://gef.es/images/revista/revista-espanola-mecanica-fractura-vol4-julio2022.pdf info:eu-repo/grantAgreement/Junta de Castilla y León//BU-002-P20//Optimización de las técnicas de post-procesado para la mejora de propiedades mecánicas y de fatiga en componentes realizados mediante fabricación aditiva/ info:eu-repo/semantics/openAccess application/pdf Sociedad Española de Integridad Estructural. Grupo Español de Fractura