2026-04-28T03:00:12Zhttps://riubu.ubu.es/oai/request

oai:riubu.ubu.es:10259/97242024-11-22T01:05:18Zcom_10259_6171com_10259_5086com_10259_2604col_10259_6172

¿Por qué el efecto del árido de hormigón reciclado en la resistencia a compresión del hormigón autocompactante no es homogéneo? Una revisión bibliográfica Why is the effect of recycled concrete aggregate on the compressive strength of self-compacting concrete not homogeneous? A bibliographic review Revilla Cuesta, Víctor Ortega López, Vanesa Skaf Revenga, Marta Fiol Olivan, Francisco Manso Villalaín, Juan Manuel Hormigón autocompactante Árido de hormigón reciclado Resistencia a compresión Dispersión de resistencia Sostenibilidad Self-compacting concrete Recycled concrete aggregate Compressive strength Strength dispersion Sustainability Resistencia de materiales Materiales de construcción Strength of materials Building materials La presente revisión bibliográfica profundiza en cómo las características del Árido de Hormigón Reciclado (AHR) afectan al comportamiento resistente del Hormigón AutoCompactante (HAC) y cómo el efecto esperado del AHR puede alterarse por cambios en la composición del HAC. Se demuestra que, si la trabajabilidad del HAC se mantiene constante, la resistencia a compresión disminuye linealmente con el contenido de AHR, aunque este descenso será menor si el AHR procede del machaqueo de un hormigón de mayor resistencia. La disminución de la relación agua/cemento permite compensar esta pérdida de resistencia, aunque su valor debe permitir también mantener una adecuada trabajabilidad del HAC. La absorción de agua del AHR y su interacción con otros compontes incrementan la variabilidad del efecto del AHR. Debido a la gran cantidad de factores implicados en este comportamiento, es recomendable un estudio experimental del AHR y del HAC producido con él antes de su utilización. This literature review deepens in how the properties of Recycled Concrete Aggregate (RCA) affect the strength behavior of Self-Compacting Concrete (SCC) and how the expected effect of RCA can be modified by changes in its composition. It is demonstrated that, if the flowability of the SCC remains constant, the compressive strength decreases linearly with the RCA content, although this decrease is lower if the RCA is obtained from the crushing of a concrete with higher strength. The decrease of the water-to-cement ratio allows compensating this loss of strength, although its value should also allow keeping a suitable flowability. The water absorption of RCA and its interaction with other components of the mix increase the variability of the effect of RCA. Therefore, due to the large number of factors involved in this behavior, it is recommended to experimentally study the RCA and the SCC produced with it before its use. El presente trabajo ha sido financiado por el Ministerio de Ciencia e Innovación (MCINN), la Agencia Estatal de Investigación (AEI) y el Fondo Europeo De Desarrollo Regional (FEDER) [código ayuda FPU 17/03374]; la Junta de Castilla y León (JCyL) y el Fondo Europeo De Desarrollo Regional (FEDER) [código proyecto UIC-231; BU119P17]; la iniciativa de empleo juvenil de la Junta de Castilla y León y el Fondo Social Europeo (ESF) [código ayuda UBU05B_1274]; y, finalmente, la Universidad de Burgos (UBU) [código ayuda SUCONS, Y135.GI]. Los autores desean agradecer a todas estas instituciones su apoyo en este estudio. 2024-11-21T13:29:18Z 2024-11-21T13:29:18Z 2022-01 info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion 0020-0883 http://hdl.handle.net/10259/9724 10.3989/ic.87668 1988-3234 spa Informes de la Construcción. 2022, V. 74, n. 565, e435 https://doi.org/10.3989/ic.87668 info:eu-repo/grantAgreement/MICIU/Plan Estatal de Investigación Científica y Técnica y de Innovación 2013-2016/FPU17%2F03374/ info:eu-repo/grantAgreement/Junta de Castilla y León//BU119P17//Innovación Competitiva en la Utilización de Escorias Siderúrgicas para la elaboración de Hormigones de Altas Prestaciones. Aplicaciones en la Industrialización/ info:eu-repo/grantAgreement/Junta de Castilla y León//UBU05B_1274/ Atribución 4.0 Internacional http://creativecommons.org/licenses/by/4.0/ info:eu-repo/semantics/openAccess application/pdf CSIC